Contact sensitization to iron: A potentially underestimated metal allergen and elicitor of complications in patients with metal implants

Oppel, Eva ; Kapp, Florian; Böhm, Ann-Sophie; Pohl, Ralf; Thomas, Peter und Summer, Burkhard (2022): Contact sensitization to iron: A potentially underestimated metal allergen and elicitor of complications in patients with metal implants. In: Contact Dermatitis, Vol. 86, No. 6: pp. 531-538

Abstract

Background Little is known about sensitization to iron (Fe) in private, occupational, and medical settings, particulary implantology. Objectives To investigate sensitization to metals, particularly to Fe, both in pre-implant individuals with presumed metal allergy and in patients with suspected metal implant allergy. To further characterize Fe-sensitized individuals. Methods Analysis of patch-test reactions to an Fe (II) sulfate-containing metal series in 183 consecutive patients (41 pre-implant, 142 metal implant bearers). Test readings were on day (D)2, D3, and D6. Evaluation of questionnaire-aided history of metal reactivity patterns and demographics of Fe reactors. Results Metal reactivity in pre-implant/implant/total group was: to nickel 39%/30%/32%;to cobalt 17%/15%/15%;and to chromium 7%/13%/11%. Co-sensitizations cobalt/nickel (19/58) and cobalt/chromium (11/21) were significant at P < .001;co-sensitizations Fe/nickel (4/10) and chromium/knee arthroplasty (11/73) at P = .03. Ten of 183 (5.5%) reacted to Fe (2 of 41 pre-implant patients, 8 of 142 implant bearers), with 10 reacting only on D6. Fe reactivity was highest in complicated knee arthroplasty (7/73). Further peculiarities of Fe reactors included frequent isolated Fe reactivity (6/10), occupational metal exposure (7/10), previous (par)enteral Fe substitution (6/10). Conclusions The 5.5% prevalence of Fe reactions suggests a potentially underestimated role of this metal allergen in general and in implant bearers. The latter also shows a distinct metal sensitization pattern.

• Item Type: Journal article
• Faculties: Medicine
• Subjects: 600 Technology > 610 Medicine and health
• ISSN: 0105-1873
• Language: English
• DFG: Gefördert durch die Deutsche Forschungsgemeinschaft (DFG) - 491502892