Is the high-performance thermoplastic polyetheretherketone indicated as a clasp material for removable dental prostheses?

Micovic, Danka; Mayinger, Felicitas; Bauer, Sebastian; Roos, Malgorzata; Eichberger, Marlis und Stawarczyk, Bogna (2020): Is the high-performance thermoplastic polyetheretherketone indicated as a clasp material for removable dental prostheses? In: Clinical Oral Investigations, Bd. 25, Nr. 5: S. 2859-2866

Abstract

Objectives: To investigate the retention force of polyetheretherketone (PEEK) removable dental prosthesis clasps in comparison with a cobalt-chrome-molybdenum control group after storage in artificial saliva. Materials and Methods Clasps were milled (Dentokeep (PEEKmilled1), NT digital implant technology;breCAM BioHPP Blank (PEEKmilled2), bredent), pressed (BioHPP Granulat for 2 press (PEEKpressed), bredent), or cast (remanium GM 800+ (cobalt-chrome-molybdenum), Dentaurum);N= 60,n= 15/subgroup. Retention force was examined 50 times/specimen in a pull-off test using the universal testing machine (Zwick 1445), where pull-off force was applied with a crosshead speed of 5 mm/minute until the maximum force dropped by 10%, at different aging levels: (1) initial, after storage in artificial saliva for (2) 90 and (3) 180 days. Statistical analysis was performed using one-way ANOVA followed by post hoc Scheffe-test and mixed models (p< 0.05). Results: Cobalt-chrome-molybdenum presented the highest retention force. No differences were observed between polyetheretherketone materials. Cobalt-chrome-molybdenum showed a significant decrease of its values after artificial aging, while polyetheretherketone materials presented similar results over the course of aging. Regarding a repetitive insertion and removal, even though PEEKmilled2 and cobalt-chrome-molybdenum showed an initial increase, ultimately, a decrease in retention force was observed for all tested groups. Conclusions: Although the control group showed significantly higher results, the retention force of polyetheretherketone materials indicate a potential clinical application. Neither the manufacturing process nor artificial aging showed an impact on the retention force of polyetheretherketone clasps.

• Dokumententyp: Zeitschriftenartikel
• Fakultät: Medizin
• Themengebiete: 600 Technik, Medizin, angewandte Wissenschaften > 610 Medizin und Gesundheit
• ISSN: 1432-6981
• Sprache: Englisch