Translucency, flexural strength, fracture toughness, fracture load of 3-unit FDPs, Martens hardness parameter and grain size of 3Y-TZP materials

Luemkemann, Nina; Pfefferle, Regina; Jerman, Eva; Sener, Beatrice und Stawarczyk, Bogna (2020): Translucency, flexural strength, fracture toughness, fracture load of 3-unit FDPs, Martens hardness parameter and grain size of 3Y-TZP materials. In: Dental Materials, Bd. 36, Nr. 7: S. 838-845

Abstract

Objective. This investigation tested pre-shaded 3Y-TZP materials on optical, mechanical and structural properties and calculated correlations between these properties. Methods. Seven A2-shaded 3Y-TZP zirconia materials were investigated on translucency (T) via UV-vis-spectrophotometer, fracture load of 3-unit FDPs (FL), biaxial flexural strength (FS), Chevron-Notch Beam (CNB), fracture toughness (KO and Martens parameter (hardness: HM and indentation modulus: E-IT). FL, FS and K-IC were measured in a universal testing machine. The grain size was evaluated by scanning electron microscopy (SEM). Data was analyzed using one-way ANOVA followed by post hoc Scheffe, Kruskal-Wallis-, Mann-Whitney-U-and Pearson-test (p < 0.05). Results. For translucency, negative correlations were found with results of facture load (R = -0.444, p < 0.001) and K-IC (R = -0.503, p < 0.001). While a positive correlation was found between translucency and flexural strength (R = 0.238, p = 0.019), between fracture load and E-IT (R = 0.227, p <0.029), between fracture load and K-IC (R = 0.362, p < 0.001) as well as between fracture load and the grain size (R = 0.598, p = 0.007). While the grain size positively correlated with E-IT (R = 0.534, p = 0.017) as well as E-IT with HM (R = 0.720, p < 0.001). Significance. Despite of being based on the same raw material, tested zirconia materials significantly differed regarding optical, mechanical (except biaxial flexural strength and Martens hardness) and structural properties. Materials with highest optical properties were those with lowest mechanical properties (CER, COP). (C) 2020 The Academy of Dental Materials.

• Dokumententyp: Zeitschriftenartikel
• Fakultät: Medizin
• Themengebiete: 600 Technik, Medizin, angewandte Wissenschaften > 610 Medizin und Gesundheit
• ISSN: 0109-5641
• Sprache: Englisch