Self-limiting caries excavation with a polymer bur: Adhesive bonding to residual dentin

Wohlleb, Teresa; Kaisarly, Dalia; Roesch, Peter und Kunzelmann, Karl-Heinz (2020): Self-limiting caries excavation with a polymer bur: Adhesive bonding to residual dentin. In: International Journal of Adhesion and Adhesives, Bd. 98, 102509

Abstract

Objectives: The aim of this study was to evaluate the bonding of an universal adhesive to residual affected dentin after polymer bur excavation of natural caries lesions in human teeth. Materials and methods: Caries excavation with a polymer bur and with a carbide bur were compared. A micro-tensile bond strength (mu-TBS) test was performed in a split-tooth design (n = 20/group). A universal adhesive (Scotchbond Universal, 3M-Deutschland, Neuss/Germany) was applied in either self-etch (SE) or total-etch (TE) mode. Qualitative and quantitative margin analysis was assessed before/after fatigue simulation (n = 8/group). Micro-CT examination was performed before/after polymerization of class-II restorations (Tetric EvoCeram BulkFill, Ivoclar-Vivadent, Schaan/Liechtenstein) (n = 6/group). Volumetric shrinkage and shrinkage vectors were calculated. The internal interface was analyzed under scanning electron microscopy after cutting the teeth. Results: The mu-TBS test revealed no significant difference between excavation methods. Mean tensile strengths (MPa) were: polymer-bur/SE = 16.0, polymer-bur/TE = 16.7, carbide-bur/SE = 15.5, carbide-bur/TE = 20.3, dentin/SE = 13.9, dentin/TE = 24.1. Margin analysis rated all groups >99% of perfect margin in dentin and enamel, no influence of excavation methods was found. Micro-CT examination revealed no difference between groups concerning volumetric shrinkage (1.9-2.5%). The shrinkage direction was towards the bonded area. Polymer bur excavation resulted in an irregular surface and thicker smear layer than with carbide bur. Conclusion: Caries excavation with a polymer bur does not negatively affect bonding performance to residual affected dentin. Etching with phosphoric acid can further strengthen the interface.

• Dokumententyp: Zeitschriftenartikel
• Fakultät: Medizin
• Themengebiete: 600 Technik, Medizin, angewandte Wissenschaften > 610 Medizin und Gesundheit
• ISSN: 0143-7496
• Sprache: Englisch